Introduction to raw materials
SLC MATERIAL
List of raw materials
| No. | Product | Color | Binder | Lubricant | Thinner | Hardening Temperature | Hardening Time | Applications | Characteristics |
|---|---|---|---|---|---|---|---|---|---|
| 1 | SLC 203 | Black(semi-gloss) | Epoxy series | PTFE | MEK | 180℃ | 30min | Car safe belts | Medium-term anti-corrosive power, load carrying capacity |
| 2 | SLC 203M | Black(semi-gloss) | PAI series | PTFE | DMAC | 220℃ | 30min | Car brake systems/ office equipment | Excellent pencil hardness |
| 3 | SLC 501B | Blue | Organic binder | PTFE | WATER, IPA | 150℃ | 30min | Car O-rings | Low friction coefficient, used for rubber and plastic |
| 4 | SLC 501K-12 | Dusky | Organic binder | PTFE | WATER, IPA | 150℃ | 30min | Car rubber parts | Excellent release property, applied to various rubber goods |
| 5 | SLC 203S | Silver | Epoxy series | PTFE | MEK | 180℃ | 30min | Cars | |
| 6 | SLC 204S | Silver | Epoxy series | PTFE | MEK | 180℃ | 30min | Cars | Gaskets, heat resistance |
| 7 | SLC 209HM | Black(matt) | Epoxy series | PTFE | MEK | 180℃ | 30min | Car brake systems | Excellent pencil hardness |
| 8 | SLC 210 | Black (matt) | Epoxy series | PTFE | MEK | 180°C | 30min | Car brake systems/office equipment | Low friction coefficient, excellent pencil hardness |
| 9 | SLC 211 | Black (semi-gloss) | Epoxy series | PTFE | DMAC | 180°C | 30min | Car brake systems | Excellent pencil hardness |
| 10 | SLC 110S | Silver | Organic binder | B/N | WATER, IPA | 150°C | 30min | Car turbo gaskets | Heat resistance |
| 11 | SLC 109 | Ivory | Organic binder | B/N | WATER, IPA | 150°C | 30min | Car turbo gaskets | Heat resistance |
| 12 | SLC 900 | Dusky | Organic binder | MoS2 | Normal temperature drying | Early taming | Convenient use, bolt sticking prevention, cold forging | ||
| 13 | SLC 901 | Dusky | Epoxy series | MoS2 | MEK | 180°C | 30min | Car gaskets | High load |
| 14 | SLC 902 | Dusky | Epoxy series | MoS2 | MEK | 180°C | 30min | Car start motors | High load |
| 15 | SLC 306 | Black (semi-gloss) | PAI series | MoS2 | DMAC | 220°C | 30min | Car start motors | Excellent adhesive strength, long-term lubrication |
| 16 | SLC 903 | Dusky | Epoxy series | Graphite | MEK | 180°C | 30min | Car start motors | Load carrying capacity, long- term lubrication |
| 17 | SLC 130 | Dusky | PAI series | PEEK | DMAC | 400°C | 20min | Compressor screws | Powerful coating formation. |
| 18 | SLC 150 | Black | Organic resin (rubber) | Rubber | MEK | 180°C | 30min | Rubber coating | Rubber coating on metal surface |
| 19 | SLC 720A | Black | Organic resin | Graphite | WATER, IPA | 120°C | 20min | Car wiper rubber | Excellent wiping capacity |
| 20 | SLC 712 | Black | Organic resin | Graphite | WATER, IPA | 120°C | 20min | Car wiper rubber | Water-repellent coatings |
| 21 | SLC 815 | Black | Organic resin | Graphite | WATER, IPA | 120°C | 20min | Car wiper rubber | Water-repellent coatings |
| 22 | SLC 803 | Black | Epoxy series | PTFE | MEK | 180°C | 30min | Car engine pistons | Silk screens |